Title: POLYMER MODIFIED HOT MIX ASPHALT FIELD TRIAL
Abstract: A problem plaguing hot mix asphalt (HMA) pavements is rutting, which develops because of the high summer temperatures and heavy trucks. Many different polymer modifiers for asphalt cement have been developed to help improve both the rutting and thermal cracking problems of HMA by altering the properties of the asphalt cement binder. The primary objective of this research was to evaluate the engineering properties and performance, especially rut resistance, of dense graded HMA containing specific polymer modifiers. The polymer modifiers were used in the HMA for the top two pavement layers of an HMA overlay of a flexible pavement. The nine modifiers considered in this study included two crumb rubbers and one gelled asphalt. Primary conclusions and recommendations resulting from this study include the following: (1) Each polymer required mixing at a higher temperature than regular HMA. These temperatures ranged from 320 deg F to 351 deg F. (2) The modified HMA mixes were successfully produced in a normal HMA production facility. Most of the modifiers did not require a blending unit. (3) Brookfield Viscometer tests showed that the modifiers were all more viscous at the lower temperatures. (4) Results of the gyratory testing machine (GTM) tests showed that the laboratory specimens had sufficient shear strength to resist the stress state in the pavement and that the air voids were above the flushing level and were consistent with design values. (5) Results to date indicate that all the modified binders are providing superior rutting resistance as compared to the control binder. This validates the wisdom of using modified binders for areas of high equivalent single axle loading (ESAL). Continued monitoring will help to better quantify the improvement provided by the modified binders. (6) The asphalt pavement analyzer (APA) test results correlate well with field rutting measurements for most of the polymer modifiers considered in this study. This indicates the potential for using the APA to predict the relative rutting performance of different polymer modifiers. Research should be conducted to substantiate this use of the APA. (7) The selection of a polymer modified asphalt binder grade based on the high temperature component of the PG designation could be quite inappropriate for a given project, especially when crumb rubber modifiers are considered for use in the HMA.
Publication Year: 1999
Publication Date: 1999-12-01
Language: en
Type: article
Access and Citation
Cited By Count: 4
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot