Title: Antibacterial, biological, and physico-mechanical properties of a 1,3,5- triacryloylhexahydro-1,3,5-triazine containing luting agent
Abstract: Data were analysed by the Student's t-test one-way ANOVA and for µSBS, three-way ANOVA with Tukey post hoc test (α=0.05).Results: CTAT showed a higher degree of conversion (immediately and after 7 days).The film thickness was in accordance with ISO 4049 in both groups.Lower cytotoxicity and lower softening solvent were observed for CTAT when compared to the control.No statistical difference was shown between the groups for flow, flexural strength, in planktonic analysis and in antibacterial activity analysis.Reduced biofilm formation was observed in the CTAT group.CTAT resulted in higher µSBS values after 7 days of storage when applied on Y-TZP ceramics. Conclusion:The experimental luting agent with TAT showed antibiofilm activity, increased degree of conversion and decreased the cytotoxicity.In addition, increased the bond strength in a Y-TZP substrate.