Title: THE EFFECTS OF IRRADIATION ON THE THERMAL PROPERTIES OF SEMI-CRYSTALLINE POLYAMIDES
Abstract: Irradiation crosslinking of semi-crystalline polyamides was performed by high energy electronswith various dosages. It is known that the melting behavior of the polymers after irradiation is acomplex phenomenon. In company with the wide angle X-ray diffraction and DSC data of irradiatedand unirradiated polyamides it is possible to develop the local order and perfection of the crystallinitiesslightly which resulted from introduction of intermolecular crosslinking amorphous region, incl-uding amorphous-crystalline interface and crystalline defect regions due to irradiation. It canbe explained that slight increase of melting temperature (T_m) and heat of fusion (△H_f) with increasingdosage for both of higher crystallinity nylon 4 and nylon 6. For irradiated lower crystallinity nylons,in contrast, the T_m and △H_f decrease obviously with increasing dosage. In this case, radiation cross-linking freeze in the pre-existing morphology, and then the prevention for reorganization duringheating is a dominant effect. The T_m from the second melting for all of the samples were depressed,corresponding with Flory theory. Therefore the crosslinks imposed on the molecules restrainedthe molecular mobility, and that not only depresses the crystallinity but also increases the imperfec-tion of crystallites when the radiated polymer melted and then recrystallized. These are also reflectedin the depression of heat and entropy of fusion as well as the appearance of double melting peakson the DSC thermograms.
Publication Year: 1985
Publication Date: 1985-01-01
Language: en
Type: article
Access and Citation
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot