Title: Surfactant Adsorption on Single-Crystal Silicon Surfaces in TMAH Solution: Orientation-Dependent Adsorption Detected by <i>In Situ</i> Infrared Spectroscopy
Abstract: This paper focuses on two aspects, <i xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">macroscopic and microscopic</i> , of pure and surfactant-added tetramethylammonium hydroxide (TMAH) wet etching. The macroscopic aspects deal with the technological/engineering applications of pure and surfactant-added TMAH for the fabrication of microelectromechanical systems (MEMS). The microscopic view is focused on the <i xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">in situ</i> observation of the silicon surface during etching in pure and surfactant-added TMAH solutions using Fourier transform infrared (FT-IR) spectroscopy in the multiple internal reflection geometry. The latter is primarily aimed at investigating the causes behind the change in the orientation-dependent etching behavior of TMAH solution when the surfactant is added. Silicon prisms having two different orientations ({110} and {100}) were prepared for comparison of the amount of adsorbed surfactant using FT-IR. Stronger and weaker adsorptions were observed on {110} and {100}, respectively. Moreover, ellipsometric spectroscopy (ES) measurements of surfactant adsorption depending on the crystallographic orientation are also performed in order to gain further information about the differences in the silicon-surfactant interface for Si{100} and Si{110}. In this paper, we determine the differences in surfactant adsorption characteristics for Si{110} and Si{100} using FT-IR and ES measurements for the first time, focusing both on the mechanism and on the technological/engineering applications in MEMS.
Publication Year: 2009
Publication Date: 2009-10-22
Language: en
Type: article
Indexed In: ['crossref']
Access and Citation
Cited By Count: 60
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot