Title: SiC particle reinforced oxynitride glass and glass-ceramic composites: Crystallization and viscoplastic forming ranges
Abstract: The viscoplastic forming and the crystallization ranges of SiC particle reinforced oxynitride glass composites were characterized. Crystallization starts beyond 1050°C, with MgAl2O4, MgSiO3, z - and δ-Y2Si2O7 as the main phases. A non-Newtonian flow behaviour was observed from 800 to 900°C, i.e. on both sides of Tg (Tg = 863°C), with n ≈ 0.6 (shear thickening). The viscosity versus temperature curves (drawn from creep tests), show that temperature must be higher than 950°C for the viscosity to be lower than 1010 Pa s. In the light of these results, the feasibility for viscoplastic forming of a 40 vol.% SiC composite was demonstrated by shaping a parabolic shell at 980°C within 30 min. Les domaines de formage viscoplastique et de cristallisation de composites particulaires à matrice verre oxyazoté renforcée par du carbure de silicium ont été caractérisés. La cristallisation débute au-delà de 1050°C avec pour phases principales MgAl2O4, MgSiO3, z - et δ-Y2Si2O7. Un écoulement de type non-newtonien a été observé dans l'intervalle 800–950°C, i.e. de part et d'autre de Tg (Tg = 863°C), avec n ≈ 0.6 (comportement rheo-épaississant). Les courbes viscosité-température obtenues par fluage montrent que la température doit être supérieure à 950°C pour que la viscosité soit inférieure à 1010 Pa s. A la lumière de ces résultats, la faisabilité de mise en forme d'un composite contenant 40% de SiC en volume a été démontrée par la réalisation d'une coque parabolique à 980°C en l'espace de 30 min.
Publication Year: 1996
Publication Date: 1996-06-01
Language: fr
Type: article
Indexed In: ['crossref']
Access and Citation
Cited By Count: 31
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot