Title: Properties of tungsten coating deposited onto copper by high-speed atmospheric plasma spraying
Abstract: Tungsten (W) coatings were fabricated on copper (Cu) by high-speed atmospheric plasma spray (HAPS) technique. The properties of the porosity, oxygen content, bonding strength and microhardness were measured. The results obtained indicated that the HAPS-W coating showed good properties particularly in terms of porosity and oxygen content. The porosity of the HAPS-W coating was 2.3% and the distribution of pore size diameter was mainly concentrated in the range of 0.01–1 μm. The oxygen content of the coating measured by means of Nitrogen/Oxygen Determinator was about 0.10 wt.%. These initial results suggest that the HAPS-W coating has achieved the reported properties of the vacuum plasma spray (VPS) W coating. Compared with VPS, HAPS-W technique could provide a convenient and low cost way to obtain adequate W coatings for fusion applications.
Publication Year: 2011
Publication Date: 2011-04-25
Language: en
Type: article
Indexed In: ['crossref']
Access and Citation
Cited By Count: 33
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot