Title: Strengthening of an L12-ordered γ′-intermetallic by disordered γ-particles. Part I: Computer simulations
Abstract: Strengthening of an L12-long-range ordered γ′-intermetallic by coherent disordered spherical γ-particles has been investigated by computer simulations and by measuring the critical resolved shear stress (CRSS) of Ni69Co9Al18Ti4. In the present Part I the simulations and their results are communicated, in Part II experimental data taken for Ni69Co9Al18Ti4 will be reported. The simulations yielded numerical values for the CRSS τp. The average radii r and the volume fractions f of the γ-particles have been varied widely: 1 nm≤r≤19 nm and 0.04≤f≤0.10. The numerical results τp (r≥7 nm, f) can be well represented by Friedel's relation—provided the dissociation of the dislocations into partial dislocations is allowed for in the calculation of the dislocation line tension. Die Härtung einer L12-ferngeordneten γ′-Phase durch kohärente, ungeordnete, kugelförmige γ-Partikel wurde im Computer simuliert, und es wurden Messungen der kritischen Schubspannung τp von Ni69Co9Al18Ti4 ausgeführt. Im vorliegenden Teil I werden die Simulationen und ihre Ergebnisse vorgestellt; in Teil II folgen Messergebnisse für Ni69Co9Al18Ti4. Die Simulationen ergaben numerische Werte für τp. Die untersuchten Wertebereiche für die mittleren Radien r der γ-Partikel und für ihren Volumenanteil f waren: 1 nm≤r≤19 nm und 0.04≤f≤0.10. Die numerischen Ergebnisse τp (r≥7 nm,f) werden durch die Friedel-Formel gut beschrieben—vorausgesetzt bei der Berechnung der Linienspannung der Versetzungen wird ihre Aufspaltung berücksichtigt.
Publication Year: 2001
Publication Date: 2001-06-01
Language: en
Type: article
Indexed In: ['crossref']
Access and Citation
Cited By Count: 18
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot