Title: The origin of defects in SiO<sub>2</sub>thermally grown on Czochralski silicon substrates
Abstract: We have observed the origin of defects in SiO2 thermally grown on Czochralski silicon substrates. Samples were prepared by copper decoration to locate oxide defects, focused ion beam etching to mark them, and subsequent silicon-substrate thinning for transmission electron microscope observation. Polyhedron structures with sizes ranging from 150 to 300 nm are found in the underlying silicon-substrate surface layer just under the oxide defects. Two polyhedron structures superimposed on each other are also observed. It is believed that these structures are related to the presence of oxygen precipitates. Oxide defects are thought to arise due to oxide thinning induced at the edge of the silicon-substrate surface adjacent to the octahedron structures.
Publication Year: 1995
Publication Date: 1995-08-01
Language: en
Type: article
Indexed In: ['crossref']
Access and Citation
Cited By Count: 35
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot