Title: Volumetric hydrogen storage in single-walled carbon nanotubes
Abstract: Macroscopically long ropes of aligned single-walled carbon nanotubes (SWNTs), synthesized by a hydrogen and argon arc discharge method, were cold pressed into tablets without any binder for measurements of their volumetric hydrogen storage capacity. The typical apparent density of the tablets was measured to be around 1.7 g/cm3 with respect to a molding pressure of 0.75 Gpa. A volumetric and mass hydrogen storage capacity of 68 kg H2/m3 and 4.0 wt %, respectively, was achieved at room temperature under a pressure of 11 MPa for suitably pretreated SWNT tablets, and more than 70% of the hydrogen adsorbed can be released under ambient pressure at room temperature. Pore structure analysis indicated that the molding process diminished the mesopore volume of the SWNT ropes, but exerts little influence on their intrinsic pore textures.
Publication Year: 2002
Publication Date: 2002-04-01
Language: en
Type: article
Indexed In: ['crossref']
Access and Citation
Cited By Count: 65
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot