Title: Influence of the Trace Boron Element on Corrosion Behavior of 1Cr17 Stainless Steel in 10% Hcl Solution
Abstract: Four groups of 1Cr17 stainless steel with diffirent wt% of boron ( 0ppm, 16ppm, 22ppm and 28ppm ) were smelted by a vacuum induction furnace. Then chemical immersion and electrochemical method (the tafel polarization curve method) were used to investigate their corrosion behavior at different temperature (25 °C, 40 °C) in HCL medium . The results show that after adding Boron elements of the 1Cr17 stainless steel sample, it is obvious that its resistance to general corrosion increases and the resistance to intergranular corrosion weakens; at different temperature (25°C, 40°C)in 10% hydrochloric acid solution medium the Corrosion kinetics law are different, while with B element content increases, the immersion corrosion rate decreases. in the reducing hydrochloric acid solution, sample with boron elements show a good behavior on corrosion resistance.
Publication Year: 2013
Publication Date: 2013-01-01
Language: en
Type: article
Indexed In: ['crossref']
Access and Citation
Cited By Count: 1
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot