Abstract: We studied the blue fluorescent OLED with Mg:Ag, Al, Ni as anode materials. Blue fluorescent OLEDs were fabricated using Anode / MoO 3 (3 nm) / 2-TNATA (60 nm) / NPB (30 nm) / SH-1 : BD-2 (5 vol.%, 30 nm) / Bphen (40 nm) / Liq (1 nm) / Al (150 nm). Current density of OLED with Mg:Ag was not measured due to too low work function, and that of OLED with Al showed 45.2 mA/cm 2 at 12 V. Luminance and Current efficiency of OLED with Al showed 385.1 cd/m 2 and 0.9 cd/A. Current density of OLED with Ni of 8, 10, 12 nm thickness showed 10, 12.9, 37.2 mA/cm 2 , respectively. Luminance and Current efficiency of OLED with Ni of 8, 10, 12 nm thickness showed 670.9, 991.2, 1,320 cd/m 2 and 6.7, 7.7, 3.6 cd/A, respectively. Transmittance of Al was 52.2% at 476 nm wavelength and that of Ni of 8, 10, 12 nm thickness was 79, 77, 74 %, respectively. In spite of best current density, OLED with Al showed the lowest luminance and current efficiency because of low work function and poor transmittance. When thickness of Ni was increased to 12nm, current efficiency was sharply lower owing to bad transmittance and unbalance of holes and electrons. Finally, OLED with Ni of 10 nm thicknes showed the highest current efficiency.
Publication Year: 2015
Publication Date: 2015-06-01
Language: en
Type: article
Access and Citation
Cited By Count: 1
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot