Title: Mechanical Properties and Fabrication of Silicon Carbide Ceramic by NITE Method
Abstract: Nano infiltration transient eutectic ceramic (NITE-SiC) was fabricated by hot pressing method using Al2O3 and Y2O3 as sintering additives. The ratio of the Al2O3/Y2O3 additives was changed between 6:4 and 4:6. The densification and mechanical properties were investigated for the sintered temperature. The starting powder was high purity β -SiC nano-powder with an average particle size of 30nm. The bending strength characterization and densification of NITE-SiC was investigated by the FE-SEM and three point bending test.