Title: Shear Bond Strength of Conventional Glass Ionomer Cements Bound to Mineral Trioxide Aggregate
Abstract: Introduction This study measured the shear bond strength of conventional glass ionomer cements (GICs; Ketac Molar Easymix and Fuji IX) bonded to white mineral trioxide aggregate (WMTA) that had been allowed to set for 2 different time intervals. Methods Forty-eight WMTA specimens were prepared; half were stored for 45 minutes, and the remaining 24 specimens were stored for 72 hours at 37 °C and 100% humidity. Then each group was divided into 2 subgroups of 12 specimens, and each GIC was layered on each of the 2 WMTA preparations. The GIC-WMTA shear bond strengths were measured and were compared by using one-way analysis of variance. Results The shear bond strengths with the 45-minute and 72-hour WMTAs were 8.85 and 9.16 MPa, respectively, for Ketac Molar Easymix and 9.34 and 9.96 MPa, respectively, for Fuji IX. The GIC-WMTA bond strength was not different between GIC applications to WMTA that had set for 45 minutes versus 72 hours (P >.05). Conclusions GICs might be used over MTA after the MTA has set for 45 minutes to allow single-visit procedures.
Publication Year: 2009
Publication Date: 2009-08-07
Language: en
Type: article
Indexed In: ['crossref', 'pubmed']
Access and Citation
Cited By Count: 38
AI Researcher Chatbot
Get quick answers to your questions about the article from our AI researcher chatbot